3M Canada

Scotch-Weld™ 021200-87838 2-Part Epoxy Adhesive, 200 mL Duo-Pak Cartridge, Part A: Light Amber/Part B: Clear, 14 days at 72 deg F Curing

7000121260 MFG #: 021200-87838
$144.94 / EA
Estimated Delivery 7 to 10 Business Days
Scotch-Weld™ 021200-87838 2-Part Epoxy Adhesive, 200 mL Duo-Pak Cartridge, Part A: Light Amber/Part B: Clear, 14 days at 72 deg F Curing
  • Manufacturer: 3M
  • Type: 2-Part
  • Container Type: Duo-Pak Cartridge
  • Container Size: 200 mL
  • Net Weight: Base: 9.3 to 9.7 lb/gal/Accelerator: 8.2 to 8.6 lb/gal
  • Base Type: Epoxy
  • Composition: Part A: Aliphatic Polymer Diamine, 4,7,10-Trioxatridecane-1,13-Diamine, Calcium Salt, Toluene/Part B: Epoxy Resin (25068-38-6), Epoxy Resin (30583-72-3)
  • Form: Viscous Liquid
  • Application Time: 80 min
  • Setting Time: 6 hr
  • Curing Time: 14 Days at 72 deg F
  • Color: Part A: Light Amber/Part B: Clear
  • Odor/Scent: Part A: Slight Amine/Part B: Slight/Epoxy
  • Temperature Rating: 72 deg F
  • Specific Gravity: Part A: 1.03/Part B: 1.17
  • Flash Point: >/=200 deg F
  • Mixing Ratio: 0.042361111111111106
  • VOC Content: <5 g/L
  • Viscosity Rating: Part A: 7000 to 15000 cPs/Part B: 2000 to 8000 cPs
  • Flammability Rating: 1
  • Applicable Materials: ABS, Acrylic, Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, PVC, Polyolefin and Thermoplastic Elastomer and Wood
  • Tensile Strength: 2750 psi
  • Shear Strength: 1200 psi
  • Brand: Scotch-Weld™
Scotch-Weld™ Epoxy Adhesive, 2-Part, Duo-Pak Cartridge Container, 200 mL Container, Epoxy Base, Composition: Part A: Aliphatic Polymer Diamine, 4,7,10-Trioxatridecane-1,13-Diamine, Calcium Salt, Toluene/Part B: Epoxy Resin (25068-38-6), Epoxy Resin (30583-72-3), 80 min Work Life, 6 hr Functional Cure, 14 days at 72 deg F Curing, Part A: Light Amber/Part B: Clear, 72 deg F, 1:1 Mixing Ratio, <5 g/L VOC, For Use On: ABS, Acrylic, Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, PVC, Polyolefin and Thermoplastic Elastomer and Wood
QTY
Add to List
  • Features high flexibility and elongation
  • Capable of bonding to a wide variety of different materials
  • Delivers extended worklife, providing additional time for adjustment
  • Low viscosity and self-leveling
  • Provides tough, strong bonds through high shear and peel strength
Features high flexibility and elongation
Capable of bonding to a wide variety of different materials
Delivers extended worklife, providing additional time for adjustment
Low viscosity and self-leveling
Provides tough, strong bonds through high shear and peel strength