Scotch-Weld™ 021200-56659 2-Part Structural Adhesive, 43 mL Cartridge, Gray, 7 days at 72 deg F Curing
7000046357
MFG #: 021200-56659
$40.56
/ EA
Estimated Delivery 7 to 10 Business Days
- Manufacturer: 3M
- Type: 2-Part
- Container Type: Cartridge
- Container Size: 43 mL
- Net Weight: Base: 11.1 to 11.6 lb/gal/Accelerator: 10.5 to 11 lb/gal
- Base Type: Epoxy
- Composition: Part A: Aliphatic Polymer Diamine, Kaolin, Bis 3-Aminopropyl) Ether of Diethylene Glycol, Toluene/Part B: Epoxy Resin, Kaolin
- Form: Viscous Liquid
- Coverage: 320 sq-ft/gal
- Drying Time: 15 min Air/10 min Force
- Application Time: 90 min
- Setting Time: 10 hr
- Curing Time: 7 Days at 72 deg F
- Color: Gray
- Odor/Scent: Part A: Pungent/Part B: Very Slight Epoxy
- Temperature Rating: 72 deg F
- Specific Gravity: Part A: 1.26/Part B: 1.33
- Flash Point: Part A: >/=201 deg F/Part B: 248 deg F
- Mixing Ratio: 0.085416666666666655
- VOC Content: 3.7 g/L
- Viscosity Rating: Part A: 40000 to 80000 cPs/Part B: 75000 to 150000 cPs
- Flammability Rating: 1
- Applicable Materials: ABS, Acrylic, Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, PVC and Wood
- Shear Strength: 3200 psi
- Brand: Scotch-Weld™
Scotch-Weld™ Structural Adhesive, 2-Part, Cartridge Container, 43 mL Container, Epoxy Base, Composition: Part A: Aliphatic Polymer Diamine, Kaolin, Bis 3-Aminopropyl) Ether of Diethylene Glycol, Toluene/Part B: Epoxy Resin, Kaolin, 90 min Work Life, 10 hr Functional Cure, 7 days at 72 deg F Curing, Gray, 72 deg F, 2:3 Mixing Ratio, 3.7 g/L VOC, For Use On: ABS, Acrylic, Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, PVC and Wood
- Maintains a strong bond under expansion, contraction and limited movement while retaining good stren
- Excellent for cryogenic bonding applications or adhering substrates that will be exposed to extreme
- Medium viscosity help minimize running, dripping, or migration while also self-leveling
- Versatile bonding agent will adhered a wide variety of similar and dissimilar substrates, including
- Can be heat cured to reduce curing times from 7 days to as a little as 30 min
Maintains a strong bond under expansion, contraction and limited movement while retaining good strength after environmental aging
Excellent for cryogenic bonding applications or adhering substrates that will be exposed to extreme cold
Medium viscosity help minimize running, dripping, or migration while also self-leveling
Versatile bonding agent will adhered a wide variety of similar and dissimilar substrates, including metals and masonry
Can be heat cured to reduce curing times from 7 days to as a little as 30 min