Simpson Strong-Tie® Crack-Pac® ETIPAC10 Injection Epoxy, 9 oz Cartridge, Blue, >250 deg F Flash

31354805 MFG #: ETIPAC10
Requires Quote
Simpson Strong-Tie® Crack-Pac® ETIPAC10 Injection Epoxy, 9 oz Cartridge, Blue, >250 deg F Flash
  • Request For Quote: Yes
Simpson Strong-Tie® Crack-Pac® Injection Epoxy, Series: ETIPAC10, 9 oz Container, Cartridge Container, Blue, 7 g/L VOC, >250 deg F Flash Point, 24 hr Curing, Bonds To: Concrete, Composition: Bisphenol A-Epichlorohydrin, Benzene-1,3-Dimethaneamine, Diethylenetriamine, 12 pH
QTY
Add to List
  • Dispenses with a standard caulking tool, no special dispensing tool needed
  • Clean and easy to mix
  • Seals out moisture, protecting rebar in the concrete from corrosion and flooring from moisture damag
  • Chemically bonds with the concrete to restore strength
  • Non-shrink material resistant to oils, salts and mild chemicals
  • Can be used to inject cracks in dry, damp or wet conditions with excellent results
  • Not for use in actively leaking cracks
  • In order for components to mix properly, the resin and hardener must be conditioned to 60 - 80 deg F
  • The color of epoxy will change from amber to blue during the cure process and then fade back to ligh
  • 1400 cP viscosity
  • 5860 psi tensile strength
  • 14% tensile elongation at break
  • 11300 psi compressive yield strength
  • 319000 psi compressive modulus
  • 8020 psi flexural strength
  • 0.08% water absorption
  • 0.002 linear coefficient of shrinkage
  • 16 min gel time
  • 30 min full, mixed cartridge
  • 8:1 mixing ratio
Dispenses with a standard caulking tool, no special dispensing tool needed
Clean and easy to mix
Seals out moisture, protecting rebar in the concrete from corrosion and flooring from moisture damage
Chemically bonds with the concrete to restore strength
Non-shrink material resistant to oils, salts and mild chemicals
Can be used to inject cracks in dry, damp or wet conditions with excellent results
Not for use in actively leaking cracks
In order for components to mix properly, the resin and hardener must be conditioned to 60 - 80 deg F before mixing
The color of epoxy will change from amber to blue during the cure process and then fade back to light amber within a few weeks of installation
1400 cP viscosity
5860 psi tensile strength
14% tensile elongation at break
11300 psi compressive yield strength
319000 psi compressive modulus
8020 psi flexural strength
0.08% water absorption
0.002 linear coefficient of shrinkage
16 min gel time
30 min full, mixed cartridge
8:1 mixing ratio