Scotch-Weld™ 021200-41529 2-Part Epoxy Adhesive, 400 mL Duo-Pak Cartridge, Black, 24 hr at 72 deg F Curing
7100077148
MFG #: 021200-41529
$425.08
/ EA
Estimated Delivery 7 to 10 Business Days
- Manufacturer: 3M
- Type: 2-Part
- Container Type: Duo-Pak Cartridge
- Container Size: 400 mL
- Net Weight: Base: 9.3 to 9.7 lb/gal/Accelerator: 9 to 9.4 lb/gal
- Base Type: Epoxy
- Composition: Modified Epoxy Resin, 4,7,10-Trioxatridecane-1,13-Diamine, Amorphous Silica, Calcium Salt, 2,4 6-Tris((Dimethylamino Methyl))Phenol
- Form: Flowable Liquid
- Drying Time: 15 min Air/10 min Force
- Application Time: 20 min
- Setting Time: 2 hr
- Curing Time: 24 hr at 72 deg F
- Color: Black
- Odor/Scent: Slight Amine
- Temperature Rating: 72 deg F
- Specific Gravity: 1.1299999999999999
- Flash Point: 340 deg F
- Mixing Ratio: 0.084027777777777771
- Viscosity Rating: 30000 cPs
- Flammability Rating: 1
- Applicable Materials: Ceramic, Glass and Metal
- Shear Strength: 4500 psi
- Brand: Scotch-Weld™
Scotch-Weld™ Epoxy Adhesive, 2-Part, Duo-Pak Cartridge Container, 400 mL Container, Epoxy Base, Composition: Modified Epoxy Resin, 4,7,10-Trioxatridecane-1,13-Diamine, Amorphous Silica, Calcium Salt, 2,4 6-Tris((Dimethylamino Methyl))Phenol, 20 min Work Life, 2 hr Functional Cure, 24 hr at 72 deg F Curing, Black, 72 deg F, 2:1 Mixing Ratio, For Use On: Ceramic, Glass and Metal
- Toughened for impact and fatigue resistance
- 20 min worklife provides time for positioning and adjustment
- Adhesive cures at room temperature, making it a convenient and easy to use solution for challenging
- Reaches high strength quickly with heat cure
- High peel and shear strength maintains enduring bond at both and low temperatures
- Medium viscosity, self-leveling formula provides easy, precise dispensing
Toughened for impact and fatigue resistance
20 min worklife provides time for positioning and adjustment
Adhesive cures at room temperature, making it a convenient and easy to use solution for challenging applications
Reaches high strength quickly with heat cure
High peel and shear strength maintains enduring bond at both and low temperatures
Medium viscosity, self-leveling formula provides easy, precise dispensing