Scotch-Weld™ 021200-87833 2-Part Part Epoxy Adhesive, 400 mL Duo-Pak Cartridge, Part A: Amber/Part B: White, 24 hr at 72 deg F Curing
7100002516
MFG #: 021200-87833
$335.51
/ EA
Estimated Delivery 7 to 10 Business Days
- Manufacturer: 3M
- Type: 2-Part Part
- Container Type: Duo-Pak Cartridge
- Container Size: 400 mL
- Net Weight: Base: 9.3 to 9.7 lb/gal/Accelerator: 9 to 9.4 lb/gal
- Base Type: Epoxy
- Composition: Part A: Modified Epoxy Resin, 4,7,10-Trioxatridecane-1,13-Diamine, Amorphous Silica, Calcium Salt, 2,4 6-Tris((Dimethylamino Methyl))Phenol, Amorphous Silica, Calcium Salt/Part B: Epoxy Resin, Acrylic Polymer
- Form: Paste
- Drying Time: 15 min Air/10 min Force
- Application Time: 20 min
- Setting Time: 2 hr
- Curing Time: 24 hr at 72 deg F
- Color: Part A: Amber/Part B: White
- Odor/Scent: Part A: Very Mild Pungent/Part B: Very Mild
- Temperature Rating: 72 deg F
- Specific Gravity: Part A: 1.12/Part B: 1.14
- Flash Point: Part A: >/=340 deg F/Part B: 480 deg F
- Mixing Ratio: 0.084027777777777771
- VOC Content: Part B: 5 g/L
- Viscosity Rating: Part A: 8000 to 14000 cPs/Part B: 20000 to 50000 cPs
- Flammability Rating: 1
- Applicable Materials: Ceramic, Glass and Metal
- Shear Strength: 4500 psi
- Brand: Scotch-Weld™
Scotch-Weld™ Epoxy Adhesive, 2-Part Part, Duo-Pak Cartridge Container, 400 mL Container, Epoxy Base, Composition: Part A: Modified Epoxy Resin, 4,7,10-Trioxatridecane-1,13-Diamine, Amorphous Silica, Calcium Salt, 2,4 6-Tris((Dimethylamino Methyl))Phenol, Amorphous Silica, Calcium Salt/Part B: Epoxy Resin, Acrylic Polymer, 20 min Work Life, 2 hr Functional Cure, 24 hr at 72 deg F Curing, Part A: Amber/Part B: White, 72 deg F, 2:1 Mixing Ratio, Part B: 5 g/L VOC, For Use On: Ceramic, Glass and Metal
- Toughened for impact and fatigue resistance
- 20 min worklife provides time for positioning and adjustment
- Adhesive cures at room temperature, making it a convenient and easy to use solution for challenging
- Reaches high strength quickly with heat cure
- High peel and shear strength maintains enduring bond at both and low temperatures
- Medium viscosity, self-leveling formula provides easy, precise dispensing
Toughened for impact and fatigue resistance
20 min worklife provides time for positioning and adjustment
Adhesive cures at room temperature, making it a convenient and easy to use solution for challenging applications
Reaches high strength quickly with heat cure
High peel and shear strength maintains enduring bond at both and low temperatures
Medium viscosity, self-leveling formula provides easy, precise dispensing