Scotch-Weld™ 021200-87274 2-Part Part Epoxy Adhesive, 200 mL Duo-Pak Cartridge, Part A: Gray/Part B: White, 48 hr at 72 deg F Curing
7000121312
MFG #: 021200-87274
$147.77
/ EA
Estimated Delivery 7 to 10 Business Days
- Manufacturer: 3M
- Type: 2-Part Part
- Container Type: Duo-Pak Cartridge
- Container Size: 200 mL
- Net Weight: Base: 9.1 to 9.4 lb/gal/Accelerator: 9 to 9.3 lb/gal
- Base Type: Epoxy
- Composition: Part A: Mercaptan Polymer, Polyamide Resin, Modified Epoxy Resin, Hydrogenated Terphenyl, 2,4,6-tris[(Dimethylamino)Methyl]Phenol, Hydrogenated Polyphenyls, Triethylenetetramine, Carbon Black/Part B: Epoxy Resin, Methacrylate/Butadiene/Styrene Polymer, Hy
- Form: Paste
- Coverage: 320 sq-ft/gal
- Drying Time: 15 min Air/10 min Force
- Application Time: 8 to 13 min
- Setting Time: 20 min
- Curing Time: 48 hr at 72 deg F
- Color: Part A: Gray/Part B: White
- Odor/Scent: Very Slight
- Temperature Rating: 72 deg F
- Specific Gravity: Part A: 1.1/Part B: 1.14
- Flash Point: Part A: 480 deg F/Part B: >/=480 deg F
- Mixing Ratio: 0.042361111111111106
- Viscosity Rating: Part A: 30000 to 70000 cPs/Part B: 45000 to 65000 cPs
- Flammability Rating: 1
- Applicable Materials: Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, Polyolefin, Thermoplastic Elastomer and Wood
- Shear Strength: 3500 psi
- Brand: Scotch-Weld™
Scotch-Weld™ Epoxy Adhesive, 2-Part Part, Duo-Pak Cartridge Container, 200 mL Container, Epoxy Base, Composition: Part A: Mercaptan Polymer, Polyamide Resin, Modified Epoxy Resin, Hydrogenated Terphenyl, 2,4,6-tris[(Dimethylamino)Methyl]Phenol, Hydrogenated Polyphenyls, Triethylenetetramine, Carbon Black/Part B: Epoxy Resin, Methacrylate/Butadiene/Styrene Polymer, Hydrogenated Terphenyl, Hydrogenated Polyphenyls, Titanium Dioxide, 8 to 13 min Work Life, 20 min Functional Cure, 48 hr at 72 deg F Curing, Part A: Gray/Part B: White, 72 deg F, 1:1 Mixing Ratio, For Use On: Ceramic, EPDM Rubber, Glass, Hardboard, High Performance Nylon, Metal, Polyolefin, Thermoplastic Elastomer and Wood
- Maintains high shear and peel strength
- Flexible when cured, making it a good choice for bonding dissimilar surfaces
- 10 min worklife with handling strength in approximately 20 min at room temperature
- Upon curing, final colors will vary from yellow to orange
Maintains high shear and peel strength
Flexible when cured, making it a good choice for bonding dissimilar surfaces
10 min worklife with handling strength in approximately 20 min at room temperature
Upon curing, final colors will vary from yellow to orange